SW Conversion Varnish, 2K Poly over Shellac

10/26/15       
Bob J Member

I have been using General Finish's High Performance Poly over Shellac on coffee tables etc and would like to use something more durable as far as scratch and moisture resistance and thinking about a 2k polyurethane (maybe Sherwin Williams T73V120) or Sherwood Williams Conversion Varnish -CCF24 (V84F81 bright rub). I work with mostly figured wood and use either BLO or Tung oil to enhance grain and use the shellac as a barrier coat as well as a sanding sealer. Does anyone know if the 2k poly or the conversion varnish can be used over shellac without adhesion issues, etc. and is either really more durable then the water borne GF poly.

10/26/15       #2: SW Conversion Varnish, 2K Poly over ...
shenendoah

try it and let us know how that works for you - may take a year or so;. or you can use sw's barrier coat - assuming they have one. and you can dye tint it to match the shellac you use

10/26/15       #3: SW Conversion Varnish, 2K Poly over ...
Leo G

I for one wouldn't be applying a catalyzed finish over shellac. I'd put it over a vinyl sealer.

I don't know about SW 2K, but recently I've been using MLC's Polarion 2K and it's very durable. I made the mistake of letting it cure for 3 days and then trying to sand it back hard (full fill on red oak) and it took 12 sheets of 5" 220 sandpaper to sand back a 25"x114" countertop. I got about 1 1/2 sq ft of sanding done before the paper wore out and would barely scratch the surface of the 2K. Then when we were installing it we had to scribe some large melamine cabinets to the wall and it required us to move the cabinets quite a few time around the counter. At the end we looked and not even a mar, let alone a scratch. But you have to let it cure at least 3 days before you get this resistance. On day one it actually scratches very easily, a paper bag will scratch it.

10/27/15       #4: SW Conversion Varnish, 2K Poly over ...
the google

leo - not to hijack the thread, but are you liking the full-finish (filled pores) look of the polarion? we shoot ilva 2k poly and i really like that it is a two coat system. we aim for an open-pore feel with our finish and i don't think this is possible with polarion. we were recently told by our mlc distributor about it and that it is a two sealer, two top coat system. this sucks for achieving an open-pore finish and for production times.

i'm curious as to your experiences.

to the op - yes, vinyl sealer/barrier coat is the way to go.

10/27/15       #5: SW Conversion Varnish, 2K Poly over ...
Leo G

Full fill certainly isn't a 2 and 2 finish. But I wasn't using a AAA pump at the time but an HVLP and had to thin it 20%.

Lots of sanding back hard with the sealer.

I could easily see using it thinned 5% out of a pump and doing a 1 and 1 coat. I did it on some shelves and they looked nice.

10/27/15       #6: SW Conversion Varnish, 2K Poly over ...
Bob J Member

Leo:

1. Why wouldn't you apply a catalyzed finish over shellac?

2. Never used vinyl sealers, do they work as barrier coats?

I will check out the MLC Polarion, I do like their products.

10/27/15       #7: SW Conversion Varnish, 2K Poly over ...
Leo G

General rule of thumb is to never apply a harder finish over a softer finish. A catalyzed finish is a harder finish then shellac, so you shouldn't do it.

10/31/15       #8: SW Conversion Varnish, 2K Poly over ...
John Member

I really like GF's HP Poly for it's UV package, but their Enduro Clear Poly is much harder and far more chemically durable. Sprays just as easily as HP Poly, too.

John

10/31/15       #9: SW Conversion Varnish, 2K Poly over ...
Rick Mosher  Member

Website: profinisher.blogspot.com/

There are many finishers who use catalyzed finishes over shellac but I am not one of them. One reason is if the finish fails it is automatically YOUR FAULT. No debate there, you used the wrong product and are responsible for your decision. On small jobs that may be worth the risk to you, I was working on huge jobs and that was not an acceptable risk.

Most 2k urethanes are self sealing and will probably work fine over a fully cured oil. I never like used oil under a surface finish. I really didn't see a huge difference in the look and on highly figured wood like tiger maple or anigre I used a clear stain base concentrate that was compatible with my finish, dried much faster and gave me almost the same look as the oil.

Sherwin Williams used to make an oily wood vinyl sealer that would probably work for you if they still have it.

11/1/15       #10: SW Conversion Varnish, 2K Poly over ...
Bob J Member

John,
I have used GF's Enduro Var clear poly for some applications but I really don't like it. It has no UV inhibitor, is not really clear as it leaves a slight yellow color like varnish and ,unless I am doing something wrong, it does not spray as nice a finish as the HP. I do like the HP poly but I usually build 7 coats before sanding & buff back and can only do 2 coats a day. The reason for considering SW's conversion varnish is that I was looking for something more durable and also I can put on 3 or 4 coats in one day and be done, and the finish does not need to be sanded back or buffed out.

Rick,
The clear stain base concentrate sounds interesting, have never used or heard of it. What one do you use and how do you use it? Any recommendations?

SW has (S64T70, S64T72 and SB Concentrate Base S64T78) which are clear wiping stain bases specifically formulated to work with the their Stain Colorants. S64T70 is a low solids clear stain base. S64T72 is a low solids clear stain base developed for areas requiring a lower VOC stain offering. S64T78 is a high solids clear stain base designed for making custom stain bases.

I picked up some SW's vinyl sealer T67F6 which is a catalyzed vinyl modified nitrocellulose sanding sealer. According to the SW rep it will probably work as a barrier coat. He said to test it by applying the sealer then the top coat. When dry take a razor blade and score the finish in a hash tag pattern and put some scotch tape over it and pull it off, if any adhesion issues it will show up.

11/1/15       #11: SW Conversion Varnish, 2K Poly over ...
Rick Mosher  Member

Website: profinisher.blogspot.com/

I believe I used the high solids SW clear stain base concentrate. I tried wet sanding it in like an oil finish but just wiping it on and off wet worked fine for me. Try it out and let us know what you think.

11/1/15       #12: SW Conversion Varnish, 2K Poly over ...
John Member

Bob, I didn't say EnduroVar, I said Enduro Clear Poly. Completely different animal. Sprays just as well as HP Poly (I agree with your comment that EnduroVar doesn't spray as well) and is just as clear. It is much more abrasion resistant and much higher chemical durability. I can easily spray 4 coats a day. Never found need for more.

John

11/8/15       #13: SW Conversion Varnish, 2K Poly over ...
Bob J Member

I tested BLO and Sherwin Williams high solids clear stain base concentrate to pop the grain on some Curly Maple. The clear stain base concentrate was wiped on and off wet and the BLO was applied over 10 minutes for absorption. When wet I did not see any difference in the figure pop. I let that dry one day and did not see any difference in the figure pop, in fact I think the clear stain popped the figure slightly more. I then applied SW's Vinyl Sealer catalyzed and two coats of SW's Conversion Varnish to both samples. The figure pop was as good if not better on the clear stain sample over the BLO sample.

I did do an adhesion test when dry on both samples by taking a razor blade and scored the finish in a hash tag pattern and put some scotch tape over it and pulled it off, did not see any adhesion issues.

I am going to go with the conversion varnish for some projects. The two draw backs for me are the toxic issue and the smell, so time will tell. I will try GF's Enduro Clear Poly when I get time to see how I like that.

2/7/17       #14: SW Conversion Varnish, 2K Poly over ...
Steve

We do tons of cabinet refinishing, and use Ilya 2k poly, catalyze at 10% exclusively. We prime both new, and refinished cabinets with Bin, which is white pigmented shellac. Have been doing this for years with 0 failures. We probably do around 30-40 jobs per year employing this process.

  • Post a Response to this thread
  • notify me of responses to this topic
  • To receive email notification of additions to this forum thread,
    enter your name and email address, and then click the
    "Keep Me Posted" button below.

    Please Note: If you have posted a message or response,
    do not submit this request ... you are already signed up
    to receive notification!

    Your Name:
    E-Mail Address:
    Enter the correct numbers into the field below:
     

    Date of your Birth:



    Return to top of page

    Buy & Sell Exchanges | Forums | Galleries | Site Map

    FORUM GUIDELINES: Please review the guidelines below before posting at WOODWEB's Interactive Message Boards (return to top)

  • WOODWEB is a professional industrial woodworking site. Hobbyist and homeowner woodworking questions are inappropriate.
  • Messages should be kept reasonably short and on topic, relating to the focus of the forum. Responses should relate to the original question.
  • A valid email return address must be included with each message.
  • Advertising is inappropriate. The only exceptions are the Classified Ads Exchange, Machinery Exchange, Lumber Exchange, and Job Opportunities and Services Exchange. When posting listings in these areas, review the posting instructions carefully.
  • Subject lines may be edited for length and clarity.
  • "Cross posting" is not permitted. Choose the best forum for your question, and post your question at one forum only.
  • Messages requesting private responses will be removed - Forums are designed to provide information and assistance for all of our visitors. Private response requests are appropriate at WOODWEB's Exchanges and Job Opportunities and Services.
  • Messages that accuse businesses or individuals of alleged negative actions or behavior are inappropriate since WOODWEB is unable to verify or substantiate the claims.
  • Posts with the intent of soliciting answers to surveys are not appropriate. Contact WOODWEB for more information on initiating a survey.
  • Excessive forum participation by an individual upsets the balance of a healthy forum atmosphere. Individuals who excessively post responses containing marginal content will be considered repeat forum abusers.
  • Responses that initiate or support inappropriate and off-topic discussion of general politics detract from the professional woodworking focus of WOODWEB, and will be removed.
  • Participants are encouraged to use their real name when posting. Intentionally using another persons name is prohibited, and posts of this nature will be removed at WOODWEB's discretion.
  • Comments, questions, or criticisms regarding Forum policies should be directed to WOODWEB's Systems Administrator
    (return to top).

    Carefully review your message before clicking on the "Send Message" button - you will not be able to revise the message once it has been sent.

    You will be notified of responses to the message(s) you posted via email. Be sure to enter your email address correctly.

    WOODWEB's forums are a highly regarded resource for professional woodworkers. Messages and responses that are crafted in a professional and civil manner strengthen this resource. Messages that do not reflect a professional tone reduce the value of our forums.

    Messages are inappropriate when their content: is deemed libelous in nature or is based on rumor, fails to meet basic standards of decorum, contains blatant advertising or inappropriate emphasis on self promotion (return to top).

    Libel:   Posts which defame an individual or organization, or employ a tone which can be viewed as malicious in nature. Words, pictures, or cartoons which expose a person or organization to public hatred, shame, disgrace, or ridicule, or induce an ill opinion of a person or organization, are libelous.

    Improper Decorum:   Posts which are profane, inciting, disrespectful or uncivil in tone, or maliciously worded. This also includes the venting of unsubstantiated opinions. Such messages do little to illuminate a given topic, and often have the opposite effect. Constructive criticism is acceptable (return to top).

    Advertising:   The purpose of WOODWEB Forums is to provide answers, not an advertising venue. Companies participating in a Forum discussion should provide specific answers to posted questions. WOODWEB suggests that businesses include an appropriately crafted signature in order to identify their company. A well meaning post that seems to be on-topic but contains a product reference may do your business more harm than good in the Forum environment. Forum users may perceive your references to specific products as unsolicited advertising (spam) and consciously avoid your web site or services. A well-crafted signature is an appropriate way to advertise your services that will not offend potential customers. Signatures should be limited to 4-6 lines, and may contain information that identifies the type of business you're in, your URL and email address (return to top).

    Repeated Forum Abuse: Forum participants who repeatedly fail to follow WOODWEB's Forum Guidelines may encounter difficulty when attempting to post messages.

    There are often situations when the original message asks for opinions: "What is the best widget for my type of shop?". To a certain extent, the person posting the message is responsible for including specific questions within the message. An open ended question (like the one above) invites responses that may read as sales pitches. WOODWEB suggests that companies responding to such a question provide detailed and substantive replies rather than responses that read as a one-sided product promotion. It has been WOODWEB's experience that substantive responses are held in higher regard by our readers (return to top).

    The staff of WOODWEB assume no responsibility for the accuracy, content, or outcome of any posting transmitted at WOODWEB's Message Boards. Participants should undertake the use of machinery, materials and methods discussed at WOODWEB's Message Boards after considerate evaluation, and at their own risk. WOODWEB reserves the right to delete any messages it deems inappropriate. (return to top)


  • Forum Posting Help
    Your Name The name you enter in this field will be the name that appears with your post or response (return to form).
    Your Website Personal or business website links must point to the author's website. Inappropriate links will be removed without notice, and at WOODWEB's sole discretion. WOODWEB reserves the right to delete any messages with links it deems inappropriate. (return to form)
    E-Mail Address Your e-mail address will not be publicly viewable. Forum participants will be able to contact you using a contact link (included with your post) that is substituted for your actual address. You must include a valid email address in this field. (return to form)
    Subject Subject may be edited for length and clarity. Subject lines should provide an indication of the content of your post. (return to form)
    Thread Related Link and Image Guidelines Thread Related Links posted at WOODWEB's Forums and Exchanges should point to locations that provide supporting information for the topic being discussed in the current message thread. The purpose of WOODWEB Forums is to provide answers, not to serve as an advertising venue. A Thread Related Link that directs visitors to an area with inappropriate content will be removed. WOODWEB reserves the right to delete any messages with links or images it deems inappropriate. (return to form)
    Thread Related File Uploads Thread Related Files posted at WOODWEB's Forums and Exchanges should provide supporting information for the topic being discussed in the current message thread. Video Files: acceptable video formats are: .MOV .AVI .WMV .MPEG .MPG .MP4 (Image Upload Tips)   If you encounter any difficulty when uploading video files, E-mail WOODWEB for assistance. The purpose of WOODWEB Forums is to provide answers, not to serve as an advertising venue. A Thread Related File that contains inappropriate content will be removed, and uploaded files that are not directly related to the message thread will be removed. WOODWEB reserves the right to delete any messages with links, files, or images it deems inappropriate. (return to form)